Page 21 - E-CATALOG BUMN
P. 21
SIBELHIJAU: GREEN WASTE
CONCRETE INNOVATION
Mind id | Institute Teknologi Sepuluh November
Prototype (ITS) Surabaya | 2020 - 2021
Mind id | Institute Teknologi Sepuluh November (ITS) Surabaya |
2020 - 2021
Penelitian dimulai dari optimalisasi komposisi beton mengandung bakteri dan paving, yang terdiri dari
komposisi campuran mengandung 20% FABA (fly ash dan bottom ash) dan maksimal 50% FABA. FABA
untuk pengujian berasal dari PLTU Pelabuhan Tarahan di bawah koordinasi PT Bukit Asam (Persero).
Tahap Kedua adalah penentuan produk berkinerja terbaik berdasarkan standar mutu masing-masing
produk. Tahap terakhir adalah rekomendasi produk sesuai dengan harga pokok material yang paling
ekonomis. Produk akhir yang ditargetkan adalah desain Readymix dan paving yang terbukti tidak
beracun, memenuhi standar nasional, ekonomis sekaligus dapat mengurangi limbah di PLTU serta
berpotensi diaplikasikan di lingkungan sesungguhnya. Paving direkomendasikan terbuat dari 35%
FA menggantikan semen untuk menghasilkan mutu B dengan kuat tekan rata-rata 37 MPa. Beton
yang direkomendasikan adalah dari campuran yang mengandung FA maksimal 35% dan BA 10%
menggantikan pasir dengan kandungan bakteri 400mL per meter kubik campuran beton. Produk ini
menghasilkan kuat tekan minimal 40,7 MPa di umur 28 hari.
The research was started from optimizing the composition of concrete containing bacteria and
paving, which consisted of a mixture composition containing 20% FABA (fly ash and bottom ash)
and a maximum of 50% FABA. FABA for testing comes from the PLTU Tarahan Port under the
coordination of PT Bukit Asam (Persero). The second stage is the determination of the best performing
product based on the quality standards of each product. The last stage is product recommendations
according to the most economical cost of materials. The final products targeted are Ready-mix
designs and paving which are proven to be non-toxic, meet national standards, are economical while
reducing waste in power plants and have the potential to be applied in the real environment. Paving
is recommended to be made of 35%FA instead of cement to produce B grade with an average
compressive strength of 37 MPa. The recommended concrete is generated from a mixture containing
a maximum FA of 35% and BA 10% replacing sand with a bacterial content of 400mL per cubic meter
of concrete mix. This product produces a compressive strength of at least 40.7 MPa at the age of 28
days.